New Fiberglass 316h Direct Roving Compatible with All Resins

• Loss on Ignition: 0.55%
• Breaking Strength: Higher Than 0.47n/Tex
• Transport Package: in Pallet
• Specification: 600/1200/2400/4800tex
• Trademark: JLON
• Origin: China
• HS Code: 70191200
• Production Capacity: 100000 Ton

Product Description

Product Description:
316H Direct Roving is compatible with unsaturated polyester, vinyl ester, polyurethane, and epoxy resins. It is specifically designed for pultrusion processes, especially high-speed and high-tension pultrusion processes.
316H is mainly used to reinforce electric and optical cables.

Product Features:
·Good process performance and low fuzz
·Multi-resin compatibility, complete and fast wet-out
·Excellent mechanical properties and thermal bending resistance of parts
·Excellent acid corrosion resistance

Specifications:

Glass type	E
Sizing type
Typical filament diameter (um)	13	17
Typical linear density (tex)	300 660	600 1200
Example	E6DR17-1200-316H

Technical Parameters:

Item	Linear density variation	Moisture content	Sizing content	Breakage strength
Unit	%	%	%	N/tex
Test menthod	ISO 1889	ISO 3344	ISO 1887	ISO 3341
Standard range	± 5	≤ 0.10	0.40 ± 0.10	≥ 0.40

Mechanical Properties:

Mechanical properties	Unit	Value	Resin	Test menthod
Tensile strength	MPa	2453	EP	ASTM D2343
Tensile modulus	GPa	82.0	EP	ASTM D2343

Spray up roving

Introduction:
180 assembled roving for spray up is coated with based sizing, compatible with unsaturated polyester, vinyl ester and polyurethane resins.
180 is a versatile general purpose spray up roving used to manufacture boats, yachts, sanitary ware, swimming pool and automotive parts and also pipe by centrifugal casting process.

Features:
Excellent static control
Excellent choppability and dispersion
Fast and complete wet out ensures easy roll-out and rapid air release
Excellent strength of the composite product
Excellent hydrolysis of finished product

Specifications:

Item	Specification		Standard No.
Linear density (tex)	2400±120	3000±150	ISO 1889  - 1997
Loss on ignition  ( % )	1.00±0.15	1.00±0.15	ISO 1887 - 1995
Moisture content   ( % )	≤0.1	≤0.1	ISO 3344 - 1997
Stiffness (mm)	135±15	135±15	ISO 3375 - 1997