1.2mm Thickness Pultruded Carbon Fiber Strip for Structural Strengthening

• Customization: Available
• Shape: Carbon Fiber Plate
• Raw Materials: Epoxy
• Model NO.: 1.2 T-1
• Performance: High-Strength Type
• State: Pultruded
• Mechanical Property: High-Performance Type
• Width: 50/100mm
• Tensile Strength: > 2800 MPa
• Elastic Modulus: >165 Gpa
• Elongation at Break: >1.7%
• Transport Package: Carton
• Specification: 1.2MM T-1
• Trademark: JLON
• Origin: China
• HS Code: 6815993900
• Production Capacity: 100000 M2
• Package Size: 55.00cm * 55.00cm * 10.00cm
• Package Gross Weight: 80.000kg

Product Description

Product Description:
The T-1/T-2 series carbon fiber plates are pultruded carbon fibre reinforced polymer (CFRP) laminates, designed for strengthening concrete, timber, masonry, steel andfibre reinforced polymer structures.
The T-1/T-2 series carbon fiber plates are bonded onto the structureas externally , bonded reinforcement using epoxy resin based adhesive for room temperatures curing.

Applications :
1.Increased Load Carrying Capacity:
Increasing the load capacity of floor slabs, beams and bridge sections
▪ For the installation of heavier machinery
▪ To stabilise vibrating structures
▪ For changes in building use
2.Damage to structural elements due to:
▪ Deterioration of the original construction materials
▪ Steel reinforcement corrosion
▪ Accidents (Vehicle impact, earthquakes, fire)
3.Improvement of serviceability and durability:
▪ Reduced deflection and crack width
▪ Stress reduction in the steel reinforcement
▪ Improved fatigue resistance
4.Change of the structural system:
▪ Removal of walls and / or columns
▪ Removal of floor and wall sections to create access /openings
5.Resistance to possible events:
▪Increased resistance to earthquakes, impact or explosion etc.
6.To repair design or construction defects such as:
▪ Insufficient / inadequate reinforcement
▪ Insufficient / inadequate structural depth

Advantages and Benefits:
▪ Non-corroding
▪ Very high strength
▪ Excellent durability and fatigue resistance
▪ Unlimited lengths, no joints required
▪Low system thickness, simple execution of plate intersections or crossings
▪ Easy transportation (rolls)
▪Lightweight, very easy to install, especially overhead(without temporary support)
▪Minimum preparation of plate, applicable in severallayers
▪Smooth edges without exposed fibres as result of production by pultrusion

Typical technical parameters:

Type	T-1	T-2
Nominal Thickness	1.2/1.4 mm	1.2/1.4 mm
Tensile Strength	> 2800 MPa	>2000 MPa
Elastic Modulus	>165 GPa	>140 GPa
Elongation at Break	>1.7%	>1.6%
Width	50/100 mm	50/100 mm