Introduction:
Carbon fabric is light weight, high strength and high modulus. It has good resistance to fatigue,
heat and corrosion.
Typical Uses: aviation, automobile, bicycle, surfboard, suite case, reinforcement to helmet,
buildings…
Technical Parameters:
Specifications:
Introduction:
Unidirectional woven carbon fiber fabric is produced by laying carbon fiber in warp direction and using hot melt yarn in weft direction to keep fabric stable.
Our multiaxial carbon fiber cloth include biaxial in 0/90 degree,+/-45 degree,0/90+/-45 degree or -45 degree +45 degree.Also these are unidirectional fabrics provided.
Application:
Strengthening concrete structure, brickwork and bridges
Features:
Increase of loading capacity
Repair of defects
Flexibility of surface geometry (Beams, columns, chimneys, piles, walls)
Specifications:
| Area Weight |
200 g/m2 |
300 g/m2 |
600 g/m2 |
| Fabric Design Thickness |
0.111mm |
0.167mm |
0.333mm |
| Tensile Strength |
>= 3400 MPa |
>= 3400 MPa |
>= 3400 MPa |
| Elastic Modulus |
>= 240 GPa |
>= 240 GPa |
>= 240 GPa |
| Break Elongation |
>=1.7% |
>=1.7% |
>=1.7% |
Other Specifications Available:
Fabric
Specification |
Total Weight (g/m2) |
0° |
90° |
+45° |
-45° |
Stitching Yarn (g/m2) |
|
| C-BX600-12 |
602 |
|
|
300 |
300 |
2 |
| C-BX600-50 |
602 |
|
|
300 |
300 |
2 |
| C-LT400-12 |
402 |
200 |
200 |
|
|
2 |
| C-LT600-50 |
602 |
300 |
300 |
|
|
2 |
| C-TX500-12 |
502 |
200 |
|
150 |
150 |
2 |
| C-QX600-12 |
602 |
150 |
150 |
150 |
150 |
2 |
| C-L150-12-B |
174 |
150 |
12 |
|
|
4 |
| C-T150-12-B |
176 |
|
|
150 |
10 |
8 |
| C-N150-12-B |
176 |
|
|
10 |
150 |
8 |
| C-L300-50-B |
326 |
300 |
12 |
|
|
4 |
| C-P300-12-B |
328 |
|
|
300 |
10 |
8 |
| C-N300-12-B |
328 |
|
|
10 |
300 |
8 |
| C-L600-50-B |
628 |
600 |
12 |
|
|
4 |
| C-PN260-12 |
262 |
|
|
130 |
130 |
2 |
| C-LT260-12 |
262 |
130 |
130 |
|
|
2 |
| C-PN400-12 |
402 |
|
|
200 |
200 |
|
| C-LT600-50 |
602 |
300 |
300 |
|
|
|
| C-QX400-12 |
402 |
100 |
100 |
100 |
100 |
2 |
){kind=link}