Sgp Interlayer Film for Bullet Proof Glass

• Customization: Available
• Material: Sgp
• Usage: for Laminated Glass
• Model NO.: 0.76/0.89/1.14/1.30
• Transparency: Transparent
• Feature: Moisture Proof, Heat Proof
• Hardness: Soft
• Thickness: 0.76/0.89/1.14/1.30mm
• Tear Strength: 49mj/M3
• Tensile Strength MD: 33.9 MPa
• Elongation: 385%
• Haze: <0.2%
• Yellow Index: <1.5
• Transport Package: Roll
• Specification: 0.76/0.89/1.14/1.30mm
• Trademark: JLON
• Origin: Changzhou, China
• HS Code: 3920920000
• Production Capacity: 10, 000, 000/Year
• Package Size: 130.00cm * 28.00cm * 28.00cm
• Package Gross Weight: 40.000kg

Product Description

Product Description

 

Introduction:

Compared with PVB film, SGP film (ionized interlayer film) is stronger, more transparent. It is the best choice for ultra-white glass.
The tear strength of SGP film is 5 times than that of PVB film, and hardness is 100 times than that of PVB film. It's the best material for bullet proof glass.

Application:

Bullet proof glass
Explosion proof glass

Where to use:

Cash trucks, prisons, banks, glass open air ceilings, glass stairs (good bonding to metal), glass handrails, glass bridge
 

Product Parameters

 

Specifications:

Physical Parameters		SGP		Common PVB		Test Standard
Tear(ing) Strength		49MJ/M^3		10-15MJ/M^3		ASTM  D-638
Tensile Strength		33.9Mpa		28.1Mpa		ASTM  D-638
Elongation At Break		385%		275%		ASTM-412
Proprotion		0.95		1.066		ASTM-792
Haze		<2.0%		<2.0%		JC/T  2166-2013
Yellow Index		<1.5		6-12		JC/T  2166-2013
Refractive Index		1.5		1.47-1.5		JC/T  2166-2013
Light Transmittance		89%		89%		JC/T  2166-2013
UV barrier		_		99.90%		GB15763.3-2009
Rate of Water Content		<0.1%		0.35-0.55%		SH/T 1770-2010
Melting Point		470°C		410°C		ASTM D-1929
Flame-spread Index		30		60		ASTM  E84
Combustion Index		215		350		ASTM  E84

Advanced Equipment:

Full Range of Tests: