High Silica Glass Cloth with Stitched Edges

• Surface Treatment: No Coating
• Weave Type: Plain or Twill
• Fiberglass Type: High Silica
• Sio2: >96%
• Loss on Ignition: 3%
• Soft Point: 1700
• Transport Package: in Pallet
• Specification: 200-1250gsm
• Trademark: JLON
• Origin: China
• HS Code: 70191200
• Production Capacity: 100000

Product Description

Introduction:
Silica fiberglass is a high temperature inorganic fibers that content more than 96% of SiO2, it's resistant to high temperature, soft point 1700°C, long term service temperature 900°C, and it can work 10 minutes at 1450°C and keeps good state at 1600°C for 15 seconds. For its properties of chemical stability, high temperature
resistance and ablation resistance, it is widely used in aviation and aerospace, metallurgy,
chemical, building material and fire fighting industry, etc...
Our silica fiberglass products are available in forms of needled mat, fabric, scrim, staple yarn,
chopped strand, cord, tape, sleeve, and fire blanket, etc.


Features:
SiO2≥96%
Soft point upto 1700°C, long-period service at 900°C
Low thermal conductivity
Good chemical stability
Good electrical insulation
Low thermal shrinkage
Non-asbestos product without pollution
Good process performanc

 

Product Name	High Silica Cloth		Product Code		BWT260 (Heated)
Test Item				Standard Value
Weave				Plain
Width (cm)				82-100
Thickness (mm)				0.260±0.026
Weight (g/m ^2)				240±20
Density (ends/cm)		Warp		13±0.8
		Weft		13±0.8
Tensile strength (N/25mm)		Warp		≥290
		Weft		≥190
Sio2 Content (%)				≥96
Loss on ignition (%)				≤3
Softining Point(ºC)				1700
Shrinkage(Temp 1000ºC)				1%