Unidirectional Carbon Fiber Cfrp Wrap for Bridge Structural Strengthening

• Customization: Available
• Area Weight: 300
• Weave: Unidirectioanl
• Transport Package: in Carton
• Specification: 12k300g
• Trademark: JLON
• Origin: China
• HS Code: 68159920
• Production Capacity: 100000 M2

Product Description

Introduction:
Unidirectional woven carbon fiber fabric is produced by laying carbon fiber in warp direction and using hot melt yarn in weft direction to keep fabric stable.
Our multiaxial carbon fiber cloth include biaxial in 0/90 degree,+/-45 degree,0/90+/-45 degree or -45 degree +45 degree.Also these are unidirectional fabrics provided.

Application:
Strengthening concrete structure, brickwork and bridges
Features:
Increase of loading capacity
Repair of defects
Flexibility of surface geometry (Beams, columns, chimneys, piles, walls)

Specifications:

Area Weight	200 g/m2	300 g/m2	600 g/m2
Fabric Design Thickness	0.111mm	0.167mm	0.333mm
Tensile Strength	>= 3400 MPa	>= 3400 MPa	>= 3400 MPa
Elastic Modulus	>= 240 GPa	>= 240 GPa	>= 240 GPa
Break Elongation	>=1.7%	>=1.7%	>=1.7%

Other Specifications Available:

Fabric Specification	Total Weight (g/m2)	0°	90°	+45°	-45°	Stitching Yarn (g/m2)
C-BX600-12	602			300	300	2
C-BX600-50	602			300	300	2
C-LT400-12	402	200	200			2
C-LT600-50	602	300	300			2
C-TX500-12	502	200		150	150	2
C-QX600-12	602	150	150	150	150	2
C-L150-12-B	174	150	12			4
C-T150-12-B	176			150	10	8
C-N150-12-B	176			10	150	8
C-L300-50-B	326	300	12			4
C-P300-12-B	328			300	10	8
C-N300-12-B	328			10	300	8
C-L600-50-B	628	600	12			4
C-PN260-12	262			130	130	2
C-LT260-12	262	130	130			2
C-PN400-12	402			200	200
C-LT600-50	602	300	300
C-QX400-12	402	100	100	100	100	2