Long Service Life Mfe790 Vinyl Ester Resin Epoxy Resin PU Modified Epoxy Vinyl Resin

• Customization: Available
• Surface Treatment: Smooth
• Color: Yellow
• Model NO.: 790
• Product Categories: Vinyl Ester Resin
• Molding Method: Hand Lay-up Method
• Material: Resin
• Transport Package: Drum
• Specification: 200kg/drum
• Trademark: JLON
• Origin: China
• HS Code: 39059900
• Production Capacity: 10000ton/Year
• Package Size: 50.00cm * 50.00cm * 50.00cm
• Package Gross Weight: 50.000kg

Product Description

MFE 790 EPOXY  VINYL ESTER RESIN

MFE 700 range, the 2 nd generation of MFE, it set to raise the standard even higher. They all based on a technology that delivers high temperature resistance, good wet ability and process ability, standard catalyst system.
MFE 790 is PU modified epoxy vinyl ester resin which own the mechanical properties of vinyl ester resin and meanwhile provide higher toughness and elongation.

 

Properties & Benefits
• Resistance to most acid, salt, alkali and solvents
•The flexibility, tensile properties and impact strength have been greatly improved by big molecular design and the impact strength has been increased by 40%compared with standard flexible epoxy vinyl ester resin.
• Tensile elongation at break is 12%
• Good processability and abrasion resistance
•Excellent dynamic load resistance, good impact resistance  under  cyclic  temperature,  pressure fluctuation and mechanical impact conditions, and high strength retention rate.

 

Applications
• MFE 790 epoxy vinyl ester resin can be used in most of the common application technologies associated with fiber reinforced plastic process with process hand lay-up, spray up, filament winding, pultrusion and infusion/RTM

Typical Liquid Resin Properties

Property (1)	Value
Appearance	Yellow transparent liquid
Viscosity, cps 25ºC	350-600
Gel time(2) in min (25ºC)	15-25
Styrene Content	41-45 %
Shelf Life(3), Dark, below 25ºC	6 months
Density	1.03g/ml

(1) Typical values, cannot be constructed as specifications
(2) 100 g resin with 1.2g Butanox M50 and 2.5g NL-49P (1% Cobalt),
0.5g DMA (10% Dimethylaniline)

Typical Properties (1) Resin Clear Casting (3)

Property	Value	Test Method
Tensile Strength/ MPa	50-65	ASTM D-638/ISO 527
Tensile Modulus/ GPa	2.4-2.8	ASTM D-638/ISO 527
Elongation at break, %	12.0-14.0	ASTM D-638/ISO 527
Flexural Strength/ MPa	90-110	ASTM D-790/ISO 178
Flexural Modulus / GPa	2.4-2.8	ASTM D-790/ISO 178
Heat Distortion Temperature(3)	70-80 ºC	ASTM D-648 Method A
Impact strength, J/m	500	ASTM D256
Barcol hardness	25-35	ASTM D2583/EN 59

(1) Typical property values only, not to be construed as specifications.
(3) Cure schedule: 24 hours at room temperature; 2 hours at 80ºC(4) Maximum stress: 1.8 MPa (264 psi)
 

Safety and Handling Consideration
This resin contains ingredients which could be harmful if mishandled. Contact with skin and eyes should be avoided and necessary protective equipment and clothing should be worn.
The specification is 2016 edition and may change with the technological improvement.
Material Safety Data Sheets contain health and safety information for your development of appropriate product handling procedures to protect your employees and customers.
Our Material Safety Data Sheets should be read and understood by all of your supervisory personnel and employees before using MFE vinyl ester resin in your facilities.
 

Standard package:
Non-returnable steel drums, net weight is 200kg per drum

Recommended Storage:
Drums - Store at temperatures below 25ºC. Storage life decreases with increasing storage temperature. Avoid exposure to heat sources such as direct sunlight or steam pipes. To avoid
contamination of product with water, do not store outdoors.
Keep sealed to prevent moisture pick-up and monomer loss.
Rotate stock