300g 450g Carbon Fiber Ud Fabric for Drone Components and Skateboard Laminates

• Customization: Available
• Shape: Carbon Fiber Cloth
• Raw Materials: Polyacrylonitrile-Based Carbon Fiber
• Performance: General Type
• State: Fabric
• Mechanical Property: General Type
• Customized: Customized
• Material: Carbon
• Usage: Reinforcement
• Area Weight: 100-640g
• Weave: Plain/Twill
• Carbon Fiber: 1/3/6/12K
• Transport Package: in Carton
• Specification: 120g
• Trademark: JLON
• Origin: China
• HS Code: 68159920
• Production Capacity: 100000 M2
• Package Size: 1300.00cm * 280.00cm * 280.00cm
• Package Gross Weight: 16.000kg

Product Description

Introduction:
Carbon fabric is light weight, high strength and high modulus. It has good resistance to fatigue, heat and corrosion.

Typical Uses:
aviation, automobile, bicycle, surfboard, suite case, reinforcement to helmet, buildings…

Technical Parameters:

Type	Yarn		Weave	Density(10mm)		Weight (g/m2)	Thickness (mm)	Width (cm)
	Warp	Weft		Warp	Weft
JZZ01P-100	1k	1k	plain	7.5	7.5	100	0.14	80-150
JZZ01T-100	1k	1k	twill	7.5	7.5	100	0.14	80-150
JZZ01P-120	1k	1k	plain	9	9	120	0.16	80-150
JZZ01T-120	1k	1k	twill	9	9	120	0.16	80-150
JZZ01P-140	1k	1k	plain	10.5	10.5	140	0.17	80-150
JZZ01T-140	1k	1k	twill	10.5	10.5	140	0.17	80-150
JZZ01E-140	1k	1k	Satin	12	12	160	0.18	80-150
JZZ03P-180	3k	3k	plain	4.5	4.5	180	0.28	80-150
JZZ03T-180	3k	3k	twill	4.5	4.5	180	0.28	80-150
JZZ03P-200	3k	3k	plain	5	5	200	0.3	80-150
JZZ03T-200	3k	3k	twill	5	5	200	0.3	80-150
JZZ03P-240	3k	3k	plain	6	6	240	0.32	80-150
JZZ03T-240	3k	3k	twill	6	6	240	0.32	80-150
JZZ03P-280	3k	3k	plain	7	7	280	0.34	80-150
JZZ03T-280	3k	3k	twill	7	7	280	0.34	80-150
JZZ03E-320	3k	3k	Satin	8	8	320	0.36	80-150
JZZ06P-280	6k	6k	plain	3.5	3.5	280	0.36	80-150
JZZ06T-280	6k	6k	twill	3.5	3.5	280	0.36	80-150
JZZ06P-320	6k	6k	plain	4	4	320	0.38	80-150
JZZ06T-320	6k	6k	twill	4	4	320	0.38	80-150
JZZ06P-400	6k	6k	plain	5	5	400	0.42	80-150
JZZ06T-400	6k	6k	twill	5	5	400	0.42	80-150
JZZ12P-400	12k	12k	plain	2.5	2.5	400	0.46	80-150
JZZ12T-400	12k	12k	twill	2.5	2.5	400	0.46	80-150
JZZ12P-480	12k	12k	plain	3	3	480	0.52	80-150
JZZ12T-480	12k	12k	twill	3	3	480	0.52	80-150
JZZ12P-640	12k	12k	plain	4	4	640	0.64	80-150
JZZ12T-640	12k	12k	twill	4	4	640	0.64	80-150

Other specifications are available upon request.

We also have unidirectional carbon fiber fabric for strengthening buildings/bridges. Details as below:
Introduction:
Unidirectional woven carbon fiber fabric is produced by laying carbon fiber in warp direction and using hot melt yarn in weft direction to keep fabric stable.

Application:
Strengthening concrete structure, brickwork and bridges
Features:
Increase of loading capacity
Repair of defects
Flexibility of surface geometry (Beams, columns, chimneys, piles, walls)

Specifications:

Area Weight	200 g/m2	300 g/m2	600 g/m2
Fabric Design Thickness	0.111mm	0.167mm	0.333mm
Tensile Strength	>= 3400 MPa	>= 3400 MPa	>= 3400 MPa
Elastic Modulus	>= 240 GPa	>= 240 GPa	>= 240 GPa
Break Elongation	>=1.7%	>=1.7%	>=1.7%