| Shape: | Carbon Fiber Cloth |
|---|---|
| Raw Materials: | Carbon Prepreg |
| Performance: | General Type |
| State: | Chopped Fiber |
| Mechanical Property: | General Type |
| Transport Package: | Refrigerated Containers |
| Samples: |
|---|
| Customization: |
|---|
Suppliers with verified business licenses
Audited Supplier Relying on the advantages of the group's high-performance carbon fiber materials and warp knitted fabrics, weintroduced and developed a high-precision carbon fiber multi-axial warp knitted fabric prepreg production line, with 100-600g/m2fiber area weight, T300-T800 grade unidirectional or fabric prepreg production experience, and formed a fully standardized prepreg material system. With thermosetting epoxy resins such as medium-temperature curing, flame retarding and rapid curing, the product can fully meet the demand for high-quality and high-performance prepreg in wind power, rail transit, automobile, aviation, sports goods and other fields.
| Type | Fiber | Fiber area weight g/m² | Resin content % | Prepreg area weight g/m | Width mm |
| UD150 | HFC20-25K | 150±3 | 35±2 | 231±7 | 1000~1270 |
| UD200 | HFC20-25K | 200±4 | 35±2 | 308±9 | 1000~1270 |
| UD300 | HFC20-25K | 300±6 | 35±2 | 462±14 | 1000~1270 |
| PN300 | ±45°Biaxial carbon fiber warp knitted fabric | 300 | 45±2 | 555±20 | 1000~1270 |
| LT400 | 0°/90°carbon fiber warp knitted fabric | 400 | 45±2 | 733±21 | 1000~1270 |
| TW200 | Carbon fiber twill fabric | 200 | 42±2 | 345±11 | 1000~1270 |
| Note: The types shown in this table are representative , not all , and the specific specifications should be determined according to customer requirements. |
|||||
It can be kept for a year at -18ºC.
shipment by Refrigerated containers.