PVC Foam Board 60-300kg/M³ for Aircraft

• Color: White
• Certification: RoHS, ISO, CE
• Feature: Wear-resistant, Impact-resistant, Heat-resistant
• Weight: 60-300kg/M3
• Type: Plain
• Transport Package: Carton/Pallet
• Trademark: JLON
• Origin: China
• Production Capacity: 500000/Month

Product Description

IFUCAI  cell  PVC foam board

1,Type designation: D60, D80
2,Technical Data Sheet

Test Item	Standard	Unit	Results	D60	D80
Density	ISO 845	Kg/ m³	Mean	62.07	80.8
			Range	54-69	72-92
Compressive strength	ISO 844:2006	MPa	Mean	0.996	1.72
			Msmv	0.7	1.3
Compressive modulus	ISO 844:2006	MPa	Mean	87.4	135
			Msmv	55	75
Shear strength	ISO 1922:2012	MPa	Mean	0.914	1.15
			Msmv	0.7	1.0
Shear modulus	SO 1922:2012	MPa	Mean	26.7	33.9
			Msmv	22	25
Tensile strength	ASTMC297	MPa	Mean	1.81	2.66
			Msmv	1.0	2.2
Tensile modulus	ASTMC297	MPa	Mean	96.1	130
			Msmv	45	85

Definitions
mean = arithmetic mean of type test results
msmv = manufacturer's specified minimum value
3,Product description 
The D60and D80 PVC foam as new high-strength material,with lightweight, high strength, fatigue resistance. 
4,Field of application and special limitations of the product
ThePVC foam is compatible with almost all resin systems,whichcan be expanded the application in many filed, not only widely used in wind turbine, high-speed train, the luxurious yacht, aerospace and other cutting-edgefiled,but also many undevelopedfiled of high-end include building fire prevention, heat preservation, sound insulation, etc.
Thefinish productsurface preparationno needs forcoating or seal.
5,The storage condition
1)PVC rigid structure foam should be stored in the ambient temperature is not higher than 40ºC, therange of humidity is 5%-75%.
2)In order to avoid the irregular shrinkage of theproduct, theproduct cannot be exposed to direct sunlight, and the ambient temperature and humidity around the foam are kept uniform.
3)When the storage environment is quite different from  the workshop , thePVC should bestored in the workshopmore than 24 hours before used.

Using field: