Woven Roving Combimat for Pipe Repairing

• Customization: Available
• Technique: Needle Mat
• Mat Type: Stitch Bonding Mat
• Model NO.: combimat
• Fiberglass Type: E-Glass
• Woven Roving Weight: 25oz
• Mat Weight: 8oz
• Width: Customized
• Transport Package: in Carton
• Specification: 2408
• Trademark: JLON
• Origin: China
• HS Code: 70195900
• Production Capacity: 20000 Ton
• Package Size: 100.00cm * 28.00cm * 28.00cm
• Package Gross Weight: 30.000kg

Product Description

Introduction:

Woven roving combimat is made by stitching woven fabric together with a layer of chopped strand.  

Compatible with unsaturated polyester resin, vinyl ester resin, epoxy resin and phenolic resin etc. Suitable for hand lay up, pultrusion, ,etc

A layer of polyester veil can be added to give good finish for end products.

The area weight ranges from 350g/m2 to 1700g/m2. The width is from 40mm-2600mm.

Specifications:

Product No.	Overall Density (g/m²)	Woven Roving Density (g/m²)	Chop Density (g/m²)	Polyester Yarn Density (g/m²)
WRM200/150	359.5	200	150	9.5
WRM300/300	609.5	300	300	9.5
WRM500/300	809.5	500	300	9.5
WRM500/450	959.5	500	450	9.5
WRM600/300	909.5	600	300	9.5
WRM600/450	960.71	600	450	10.71
WRM800/300	1110.71	800	300	10.71
WRM800/450	1260.71	800	450	10.71
WRM1808	896.14	612	274.64	9.5
WRM1810	926.65	612	305.15	9.5
WRM1815	1080.44	612	457.73	10.71
WRM2408	1132.35	847	274.64	10.71
WRM2410	1162.86	847	305.15	10.71
WRM2415	1315.44	847	457.73	10.71
WRM2430	1762.71	847	900	15.71

Woven roving

Introduction:
Fiberglass Woven Roving is bidirectional fabric made by interweaving direct roving. Can be compatible with unsaturated polyester, vinyl ester, epoxy and phenolic resins. With high-performance reinforcement, widely used in hand lay up to manufacture boats, vessels, plane and automotive parts, furniture and sports facilities. The area weight is from 200g/m2 to 1200g/m2. The width is from 50mm-3000mm.

Specifications

Product No.	Glass	Weight(g/m²)	Breaking Strength ≥N/25MM		Weave	Moisture Content %	L.O.I Content %
			Warp	Weft
WR200	E	200+/-10	820	700	Plain	≤0.1	0.4-0.8
WR270	E/ECR	270+/-14	1200	1000	Plain	≤0.1	0.4-0.8
WR300	E	300+/-15	1200	1200	Plain	≤0.1	0.4-0.8
WR360	E/ECR	400+/-20	1200	1150	Plain	≤0.1	0.4-0.8
WR400	E	400+/-20	1480	1380	Plain	≤0.1	0.4-0.8
WR500T	E	500+/-25	1800	1700	Twill	≤0.1	0.4-0.8
WR500	E	500+/-25	1800	1600	Plain	≤0.1	0.4-0.8
WUDT500	E	500+/-25	100	2900	Plain	≤0.1	0.4-0.8
WUDL500	E	500+/-25	2600	350	Plain	≤0.1	0.4-0.8
WUDL530	E	530+/-27	3200	800	Plain	≤0.1	0.4-0.8
WR580	E/ECR	580+/-29	1900	1600	Plain	≤0.1	0.4-0.8
WR600	E	600+/-30	1900	1800	Plain	≤0.1	0.4-.8
WR600B	E	600+/-30	1900	1850	Plain	≤0.1	0.4-0.8
WUDL600	E	600+/-30	3100	350	Plain	≤0.1	0.4-0.8
WR800	E	800+/-40	2600	2300	Plain	≤0.1	0.4-0.8
WR800A	E	864+/-43	2900	2700	Plain	≤0.1	0.4-0.8
WR1000	E	1000+/-50	2900	2900	Plain	≤0.1	0.4-0.8

Chop strand mat
Chopped strand mat is produced by chopping continuous roving into length of 5cm and randomly dispersing the cut fibers. These fibers are held together by powder or emulsion binder. It is typically used for hand lay up process. The mats are compatible with unsaturated polyester, vinyl ester and PU resins. Width ranges from 50mm to 3200mm.

Application: panels, tanks, boats, complete set of sanitary equipment, automotive parts, cooling towers, pipes etc

Specifications:

Item	Weight(g/m^2)	Binder Content(%)	Water Content(%)
EMC100	100	9-12	<0.2 (powder bonded) <0.5 (emulsion bonded)
EMC150	150	9-12	<0.2 (powder bonded) <0.5 (emulsion bonded)
EMC225	225	2-8	<0.2 (powder bonded) <0.5 (emulsion bonded)
EMC300	300	2-8	<0.2 (powder bonded) <0.5 (emulsion bonded)
EMC450	450	2-8	<0.2 (powder bonded) <0.5 (emulsion bonded)
EMC600	600	2-8	<0.2 (powder bonded) <0.5 (emulsion bonded)