5% off Good Process Performance New Fiberglass Direct Roving

• Customization: Available
• Certification: ISO
• Technique: Winding Filament Roving
• Yarn Structure: Single Yarn
• Surface Treatment: Other
• Fiberglass Type: ECR
• Linear Density: 1200/2400/4800/9600 Tex
• Filament Diameter: 17/24/31 Um
• Loss on Ignition: 0.55%
• Breaking Strength: Higher Than 0.4n/Tex
• Transport Package: in Pallet
• Specification: 1200/2400/4800tex
• Trademark: JLON
• Origin: China
• HS Code: 70191200
• Production Capacity: 100000 Ton

Product Description

Introduction:
386T Direct Roving is coated with a silane-based sizing compatible with unsaturated polyester, vinyl ester, and epoxy resins. It is designed for filament winding, pultrusion, and weaving applications. 386T is suitable for use in pipes, pressure vessels, gratings, and profiles, and the woven roving converted from it is used in boats and chemical storage tanks.

Features:
Good process performance and low fuzz
Compatible with multiple resin system
Fast wet out
Good mechanical properties
Excellent acid corrosion resistance

Specifications:

Item	Specification			Standard No.
Linear density (tex)	1200±60	2400±120	4800±240	ISO 1889  - 1997
Breaking strength (N/tex)	≥0.4	≥0.4	≥0.4	ISO 3341 - 2000
Loss on ignition  ( % )	0.55±0.15	0.55±0.15	0.55±0.15	ISO 1887 - 1995
Moisture content   ( % )	≤0.1	≤0.1	≤0.1	ISO 3344 - 1997

Spray up roving

Introduction:
180 assembled roving for spray up is coated with based sizing, compatible with unsaturated polyester, vinyl ester and polyurethane resins.
180 is a versatile general purpose spray up roving used to manufacture boats, yachts, sanitary ware, swimming pool and automotive parts and also pipe by centrifugal casting process.

Features:
Excellent static control
Excellent choppability and dispersion
Fast and complete wet out ensures easy roll-out and rapid air release
Excellent strength of the composite product
Excellent hydrolysis of finished product

Specifications:

Item	Specification		Standard No.
Linear density (tex)	2400±120	3000±150	ISO 1889  - 1997
Loss on ignition  ( % )	1.00±0.15	1.00±0.15	ISO 1887 - 1995
Moisture content   ( % )	≤0.1	≤0.1	ISO 3344 - 1997
Stiffness (mm)	135±15	135±15	ISO 3375 - 1997