Excellent Durability and Fatigue Resistance 1.2mm Thickness Pultruded Carbon Fiber Plates for Structural Strengthening, Increased Load Carrying Capacity

• Customization: Available
• Width: 50/100mm
• Tensile Strength: > 2800 MPa
• Model NO.: 1.2 T-1
• Elastic Modulus: >165 Gpa
• Elongation at Break: >1.7%
• Transport Package: Carton
• Specification: 1.2MM T-1
• Trademark: JLON
• Origin: China
• HS Code: 6815993900
• Production Capacity: 100000 M2

Product Description

Product Description

Product Description:
The T-1/T-2 series carbon fiber plates are pultruded carbon fibre reinforced polymer (CFRP) laminates, designed for strengthening concrete, timber, masonry, steel andfibre reinforced polymer structures.
The T-1/T-2 series carbon fiber plates are bonded onto the structureas externally , bonded reinforcement using epoxy resin based adhesive for room temperatures curing.

Applications :
1.Increased Load Carrying Capacity:
Increasing the load capacity of floor slabs, beams and bridge sections
▪ For the installation of heavier machinery
▪ To stabilise vibrating structures
▪ For changes in building use
2.Damage to structural elements due to:
▪ Deterioration of the original construction materials
▪ Steel reinforcement corrosion
▪ Accidents (Vehicle impact, earthquakes, fire)
3.Improvement of serviceability and durability:
▪ Reduced deflection and crack width
▪ Stress reduction in the steel reinforcement
▪ Improved fatigue resistance
4.Change of the structural system:
▪ Removal of walls and / or columns
▪ Removal of floor and wall sections to create access /openings
5.Resistance to possible events:
▪Increased resistance to earthquakes, impact or explosion etc.
6.To repair design or construction defects such as:
▪ Insufficient / inadequate reinforcement
▪ Insufficient / inadequate structural depth

Advantages and Benefits:
▪ Non-corroding
▪ Very high strength
▪ Excellent durability and fatigue resistance
▪ Unlimited lengths, no joints required
▪Low system thickness, simple execution of plate intersections or crossings
▪ Easy transportation (rolls)
▪Lightweight, very easy to install, especially overhead(without temporary support)
▪Minimum preparation of plate, applicable in severallayers
▪Smooth edges without exposed fibres as result of production by pultrusion

Typical technical parameters:

Type	T-1	T-2
Nominal Thickness	1.2/1.4 mm	1.2/1.4 mm
Tensile Strength	> 2800 MPa	>2000 MPa
Elastic Modulus	>165 GPa	>140 GPa
Elongation at Break	>1.7%	>1.6%
Width	50/100 mm	50/100 mm

Related product: Carbon Fabric

Introduction:
Woven carbon fabric is light weight, high strength and high modulus. It has good resistance to fatigue, heat and corrosion.

Typical Uses:
aviation, automobile, bicycle, surfboard, suite case, reinforcement to helmet, buildings…

Technical Parameters:

Type	Yarn		Weave	Density(10mm)		Weight (g/m2)	Thickness (mm)	Width (cm)
	Warp	Weft		Warp	Weft
JZZ01P-100	1k	1k	plain	7.5	7.5	100	0.14	80-150
JZZ01T-100	1k	1k	twill	7.5	7.5	100	0.14	80-150
JZZ01P-120	1k	1k	plain	9	9	120	0.16	80-150
JZZ01T-120	1k	1k	twill	9	9	120	0.16	80-150
JZZ01P-140	1k	1k	plain	10.5	10.5	140	0.17	80-150
JZZ01T-140	1k	1k	twill	10.5	10.5	140	0.17	80-150
JZZ01E-140	1k	1k	Satin	12	12	160	0.18	80-150
JZZ03P-180	3k	3k	plain	4.5	4.5	180	0.28	80-150
JZZ03T-180	3k	3k	twill	4.5	4.5	180	0.28	80-150
JZZ03P-200	3k	3k	plain	5	5	200	0.3	80-150
JZZ03T-200	3k	3k	twill	5	5	200	0.3	80-150
JZZ03P-240	3k	3k	plain	6	6	240	0.32	80-150
JZZ03T-240	3k	3k	twill	6	6	240	0.32	80-150
JZZ03P-280	3k	3k	plain	7	7	280	0.34	80-150
JZZ03T-280	3k	3k	twill	7	7	280	0.34	80-150
JZZ03E-320	3k	3k	Satin	8	8	320	0.36	80-150
JZZ06P-280	6k	6k	plain	3.5	3.5	280	0.36	80-150
JZZ06T-280	6k	6k	twill	3.5	3.5	280	0.36	80-150
JZZ06P-320	6k	6k	plain	4	4	320	0.38	80-150
JZZ06T-320	6k	6k	twill	4	4	320	0.38	80-150
JZZ06P-400	6k	6k	plain	5	5	400	0.42	80-150
JZZ06T-400	6k	6k	twill	5	5	400	0.42	80-150
JZZ12P-400	12k	12k	plain	2.5	2.5	400	0.46	80-150
JZZ12T-400	12k	12k	twill	2.5	2.5	400	0.46	80-150
JZZ12P-480	12k	12k	plain	3	3	480	0.52	80-150
JZZ12T-480	12k	12k	twill	3	3	480	0.52	80-150
JZZ12P-640	12k	12k	plain	4	4	640	0.64	80-150
JZZ12T-640	12k	12k	twill	4	4	640	0.64	80-150

We also have unidirectional carbon fiber fabric for strengthening buildings/bridges. Details as below:

Introduction:
Unidirectional woven carbon fiber fabric is produced by laying carbon fiber in warp direction and using hot melt yarn in weft direction to keep fabric stable.

Application:
Strengthening concrete structure, brickwork and bridges
Features:
Increase of loading capacity
Repair of defects
Flexibility of surface geometry (Beams, columns, chimneys, piles, walls)

Specifications:

Area Weight	200 g/m2	300 g/m2	600 g/m2
Fabric Design Thickness	0.111mm	0.167mm	0.333mm
Tensile Strength	>= 3400 MPa	>= 3400 MPa	>= 3400 MPa
Elastic Modulus	>= 240 GPa	>= 240 GPa	>= 240 GPa
Break Elongation	>=1.7%	>=1.7%	>=1.7%

Multiaxial Carbon Fiber Fabrics

Fabric Specification	Total Weight (g/m2)	0°	90°	+45°	-45°	Stitching Yarn (g/m2)	Binder(g/m2)
C-PN600-12	602			300	300	2
C-PN600-50	602			300	300	2
C-LT400-12	402	200	200			2
C-LT600-50	602	300	300			2
C-TX500-12	502	200		150	150	2
C-QX600-12	602	150	150	150	150	2
C-L150-12-B	174	150	12			4	8
C-P150-12-B	176			150	10	8	8
C-N150-12-B	176			10	150	8	8
C-L300-50-B	326	300	12			4	10
C-P300-12-B	328			300	10	8	10
C-N300-12-B	328			10	300	8	10
C-L600-50-B	628	600	12			4	12
C-PN260-12	262			130	130	2
C-LT260-12	262	130	130			2
C-PN400-12	402			200	200	2
C-QX400-12	402	100	100	100	100	2