Fire Resistance Structural PVC Foams for Boat Build

Density: 60/80/100kg/M3,
Dimension: 2160X1000mm, 1080X1000mm
Thickness: 3-60mm
Transport Package: in Pallet
Specification: 2160x1000 or 1080x1000
Trademark: JLON
Samples:
US$ 15/Square Meter 1 Square Meter(Min.Order)
| Request Sample
Customization:

Contact Supplier

Diamond Member Since 2018

Suppliers with verified business licenses

Manufacturer/Factory, Trading Company

Basic Info.

Model NO.
Structural Cell
Origin
China
HS Code
39211290
Production Capacity
1000000m2

Product Description

Introduction:

Cross-linked, closed cell PVC structural foam has good specific stiffness, specific strength. Compression, tensile, shear and bending strengths are excellent.
PVC foam core also has good dimensional stability and easy to process, suitable for a variety of processes. It is an ideal core material for lightweight & high-strength composite sandwich structures.
It provides excellent fatigue resistance, impact resistance and very low water absorption. Heat and sound insulation are also very good.

Features:
High performance weight ratio, good impact resistance
Resistance to many chemicals, almost no water absorption
Low flammability, self-extinguishing from fire
Suitable for a variety of composite molding methods: Vacuum infusion, spray up, hand lay-up, vacuum bagging
Good impact strength
Low resin absorption
Good sound & thermal insulation

Application:
marine, surface transport, aerospace, and wind energy industries

Specifications:
Item Standard Unit   P48 P60 P80 P100 P130 P200 P250
Density ISO 845 Kg/m3 Average 48 60 80 100 130 200 250
      Tolerance 43-55 -6,+9 ±10 ±10 ±15 ±20 ±30
Compression
Strength
ASTM D1621 MPa Average 0.60 0.9 1.4 2.0 3.0 4.8 6.2
    Minimum (0.50) (0.7) (1.15) (1.65) (2.4) (4.2) (NA)
Compression Modulus ASTM D 1621 MPa Average 48 70 90 135 170 240 300
    Minimum (35) (60) (80) (115) (145) (200) (NA)
Tensile Strength ASTM D 1623 MPa Average 0.95 1.8 2.5 3.5 4.8 7.1 9.2
    Minimum (0.8) (1.5) (2.2) (2.5) (3.5) (6.3) (NA)
Tensile ASTM D 1623 MPa Average 35 75 95 130 175 250 320
Modulus     Minimum (28) (57) (85) (105) (135) (210) (NA)
Shear ASTM C 273 MPa Average 0.55 0.76 1.15 1.6 2.2 3.5 4.5
Strength     Minimum (0.50) (0.63) (0.95) (1.4) (1.9) (3.2) (NA)
Shear ASTM C 273 MPa Average 16 20 27 35 50 85 104
Modulus     Minimum (14) (16) (23) (28) (40) (75) (NA)
Shear
Elongation
ASTM C 273 % Average
Minimum
10
(8)
20
(10)
30
(15)
40
(25)
40
(30)
40
(30)
40
(NA)
  Width mm ±5 1270 1120 1010 940 840 740 700
Standard                    
Length mm ±5 2730 2350 2160 2040 1880 1600 1500
Size
                   
Thickness mm ±0.5 5~80 5~70 3~65 3~60 3~50 3~40 3~40
 

Fire Resistance Structural PVC Foams for Boat Build
Fire Resistance Structural PVC Foams for Boat Build
Fire Resistance Structural PVC Foams for Boat Build

Fire Resistance Structural PVC Foams for Boat Build

Fire Resistance Structural PVC Foams for Boat Build
Fire Resistance Structural PVC Foams for Boat Build

 

Send your message to this supplier

*From:
*To:
avatar Mrs. Irene
*Message:

Enter between 20 to 4,000 characters.

This is not what you are looking for? Post a Sourcing Request Now