100kg/M3 PVC Foam Core for Wind Turbine Nacelle Covers

• Customization: Available
• Density: 60/80/100kg/M3,
• Dimension: 2160X1000mm, 1080X1000mm
• Thickness: 3-60mm
• Transport Package: in Pallet
• Specification: 2160x1000 or 1080x1000
• Trademark: JLON
• Origin: China
• HS Code: 39211290
• Production Capacity: 1000000m2

Product Description

Product Description of Core Materials(including PVC Foam Core, PET Foam Core and PP Honeycomb Core):

has good specific stiffness, specific strength. Compression, tensile, shear and bending strengths are excellent.PVC foam core also has good dimensional stability and easy to process, suitable for a variety of processes. It is an ideal core material for lightweight & high-strength composite sandwich structures.It provides excellent fatigue resistance, impact resistance and very low water absorption. Heat and sound insulation are also very good.



Features:
High performance weight ratio, good impact resistance
Resistance to many chemicals, almost no water absorption
Low flammability, self-extinguishing from fire
Suitable for a variety of composite molding methods: Vacuum infusion, spray up, hand lay-up, vacuum bagging
Good impact strength
Low resin absorption
Good sound & thermal insulation

Specification:

Item	Standard	Unit		P48	P60	P80	P100	P130	P200	P250
Density	ISO 845	Kg/m3	Average	48	60	80	100	130	200	250
			Tolerance	43-55	-6,+9	±10	±10	±15	±20	±30
Compression Strength	ASTM D1621	MPa	Average	0.60	0.9	1.4	2.0	3.0	4.8	6.2
			Minimum	(0.50)	(0.7)	(1.15)	(1.65)	(2.4)	(4.2)	(NA)
Compression Modulus	ASTM D 1621	MPa	Average	48	70	90	135	170	240	300
			Minimum	(35)	(60)	(80)	(115)	(145)	(200)	(NA)
Tensile Strength	ASTM D 1623	MPa	Average	0.95	1.8	2.5	3.5	4.8	7.1	9.2
			Minimum	(0.8)	(1.5)	(2.2)	(2.5)	(3.5)	(6.3)	(NA)
Tensile	ASTM D 1623	MPa	Average	35	75	95	130	175	250	320
Modulus			Minimum	(28)	(57)	(85)	(105)	(135)	(210)	(NA)
Shear	ASTM C 273	MPa	Average	0.55	0.76	1.15	1.6	2.2	3.5	4.5
Strength			Minimum	(0.50)	(0.63)	(0.95)	(1.4)	(1.9)	(3.2)	(NA)
Shear	ASTM C 273	MPa	Average	16	20	27	35	50	85	104
Modulus			Minimum	(14)	(16)	(23)	(28)	(40)	(75)	(NA)
Shear Elongation	ASTM C 273	%	Average Minimum	10 (8)	20 (10)	30 (15)	40 (25)	40 (30)	40 (30)	40 (NA)
	Width	mm	±5	1270	1120	1010	940	840	740	700
Standard
	Length	mm	±5	2730	2350	2160	2040	1880	1600	1500
Size
	Thickness	mm	±0.5	5~80	5~70	3~65	3~60	3~50	3~40	3~40

has good specific stiffness, specific strength. Compression, tensile, shear and bending strengths are excellent. PET foam core also has good dimensional stability and easy to process, suitable for a variety of processes. It is an ideal core material for lightweight & high-strength composite sandwich structures.It provides excellent fatigue resistance, impact resistance and very low water absorption. Heat and sound insulation are also very good.


Features:
High exothermic peak tempertaure resistance, up to 180C
High performance weight ratio, good impact resistance
Resistance to many chemicals, almost no water absorption
Low flammability, self-extinguishing from fire
Suitable for a variety of composite molding methods: Vacuum infusion, spray up, hand lay-up, vacuum bagging
Good impact strength
Low resin absorption
Good sound & thermal insulation

Specification:

Item	Standard	Unit		P80	P100	P120	P150	P200	P250
Density	ISO 845	Kg/m3	Average	80	100	120	150	200	250
			Tolerance	-6,+9	±10	±10	±15	±20	±30
Compression	ASTM D1621	MPa	Average	0.85	1.2	1.8	2.4	3.9	5.2
Strength			Minimum	-0.8	-1.1	-1.55	-2.2	-3.4	-4.8
Compression Modulus	ASTM D 1621	MPa	Average	73	100	115	140	200	235
			Minimum	-65	-90	-105	-125	-170	-210
Tensile Strength	ASTM D 1623	MPa	Average	1.4	1.8	2.2	2.5	3.2	4
			Minimum	-1.3	-1.6	-1.9	-2.2	-2.6	-3.6
Tensile	ASTM D 1623	MPa	Average	90	110	120	160	210	275
Modulus			Minimum	-80	-100	-105	-130	-180	-250
Shear	ASTM C 273	MPa	Average	0.55	0.8	0.9	1.25	1.7	2.05
Strength			Minimum	-0.45	-0.75	-0.8	-1.05	-1.5	-1.8
Shear	ASTM C 273	MPa	Average	13.5	23	27	35	51	70
Modulus			Minimum	-12.5	-21	-23	-30	-47	-65

 Core is a new construction material, which is made of PP based on honeycomb bionic principles. Compared with traditional materials, it has these remarkable advantages like light-weight, high compressive strength, environmentally friendly, waterproof, moisture-proof and corrosion resistant etc. Moreover, it can be attached with various of face materials (such as FRP,wood grain sheet, aluminum sheet, stainless steel sheet, marble sheet, rubber sheet etc.) . Therefore, it can extensively replace traditional materials, and it can be widely used in these areas like van, high-speed train, aerospace, yachting, home furnishing and mobile architecture etc.



Structure:
reinforce woven fabric skin + pp honeycomb core + reinforce woven fabric skin.

Skin:
standard skin: 0.7mm, special skin: 1.0mm, 1.4mm.

Core density:
80kgs/m3(standard core), 100kgs/m3, 120kgs/m3.

Core thickness:
very flexible, from 10mm to 70mm.

Surface:
Painted white one side(standard paint color),
Unpainted 
Black 
Some special color paints are available, such as green, orange, red, blue etc.

Dimension:
Max length for export: 11900mm
Max width for export: 2500mm
Thickness range: from 12mm to 70mm.

Features:
Light and Strong
Green and Environment Friendly
Waterproof
Corrosion Resistant
Sound Isolation

Specifications:

ITEM	10mm Holycore	15mm Holycore
Cell core diameter(mm)	8	8
Density(kg/cb.m)	80	80
Compressive strength(MPa)	1.90	1.85
Modulus of compression(MPa)	50.8	50.4
Shear strength(MPa)	0.58	0.55
Modulus of shearing(MPa)	25	25

APPLICATION: