PP Honeycomb Core for Yachting

• Customization: Available
• Cell Core Diameter: 8mm
• Density: 80kg/M3
• Feature1: Light & Strong
• Feature2: Green & Environment Friendly
• Feature3: Waterproof
• Feature4: Corrosion Resistant
• Feature5: Sound Isolation
• Transport Package: in Sheet
• Specification: density 80kg/m3
• Trademark: JLON
• Origin: China
• HS Code: 3926909090
• Production Capacity: 5000000m2

Product Description

Product Description of Core Materials(including PP Honeycomb,PVC Foam Core and PET Foam Core):

 Core is a new construction material, which is made of PP based on honeycomb bionic principles. Compared with traditional materials, it has these remarkable advantages like light-weight, high compressive strength, environmentally friendly, waterproof, moisture-proof and corrosion resistant etc. Moreover, it can be attached with various of face materials (such as FRP,wood grain sheet, aluminum sheet, stainless steel sheet, marble sheet, rubber sheet etc.) . Therefore, it can extensively replace traditional materials, and it can be widely used in these areas like van, high-speed train, aerospace, yachting, home furnishing and mobile architecture etc.



Structure:
reinforce woven fabric skin + pp honeycomb core + reinforce woven fabric skin.

Skin:
standard skin: 0.7mm, special skin: 1.0mm, 1.4mm.

Core density:
80kgs/m3(standard core), 100kgs/m3, 120kgs/m3.

Core thickness:
very flexible, from 10mm to 70mm.

Surface:
Painted white one side(standard paint color),
Unpainted 
Black 
Some special color paints are available, such as green, orange, red, blue etc.

Dimension:
Max length for export: 11900mm
Max width for export: 2500mm
Thickness range: from 12mm to 70mm.

Features:
Light and Strong
Green and Environment Friendly
Waterproof
Corrosion Resistant
Sound Isolation

Specifications:

ITEM	10mm Holycore	15mm Holycore
Cell core diameter(mm)	8	8
Density(kg/cb.m)	80	80
Compressive strength(MPa)	1.90	1.85
Modulus of compression(MPa)	50.8	50.4
Shear strength(MPa)	0.58	0.55
Modulus of shearing(MPa)	25	25

has good specific stiffness, specific strength. Compression, tensile, shear and bending strengths are excellent.PVC foam core also has good dimensional stability and easy to process, suitable for a variety of processes. It is an ideal core material for lightweight & high-strength composite sandwich structures.It provides excellent fatigue resistance, impact resistance and very low water absorption. Heat and sound insulation are also very good.




Features:
High performance weight ratio, good impact resistance
Resistance to many chemicals, almost no water absorption
Low flammability, self-extinguishing from fire
Suitable for a variety of composite molding methods: Vacuum infusion, spray up, hand lay-up, vacuum bagging
Good impact strength
Low resin absorption
Good sound & thermal insulation

Specification:

Item	Standard	Unit		P48	P60	P80	P100	P130	P200	P250
Density	ISO 845	Kg/m3	Average	48	60	80	100	130	200	250
			Tolerance	43-55	-6,+9	±10	±10	±15	±20	±30
Compression Strength	ASTM D1621	MPa	Average	0.60	0.9	1.4	2.0	3.0	4.8	6.2
			Minimum	(0.50)	(0.7)	(1.15)	(1.65)	(2.4)	(4.2)	(NA)
Compression Modulus	ASTM D 1621	MPa	Average	48	70	90	135	170	240	300
			Minimum	(35)	(60)	(80)	(115)	(145)	(200)	(NA)
Tensile Strength	ASTM D 1623	MPa	Average	0.95	1.8	2.5	3.5	4.8	7.1	9.2
			Minimum	(0.8)	(1.5)	(2.2)	(2.5)	(3.5)	(6.3)	(NA)
Tensile	ASTM D 1623	MPa	Average	35	75	95	130	175	250	320
Modulus			Minimum	(28)	(57)	(85)	(105)	(135)	(210)	(NA)
Shear	ASTM C 273	MPa	Average	0.55	0.76	1.15	1.6	2.2	3.5	4.5
Strength			Minimum	(0.50)	(0.63)	(0.95)	(1.4)	(1.9)	(3.2)	(NA)
Shear	ASTM C 273	MPa	Average	16	20	27	35	50	85	104
Modulus			Minimum	(14)	(16)	(23)	(28)	(40)	(75)	(NA)
Shear Elongation	ASTM C 273	%	Average Minimum	10 (8)	20 (10)	30 (15)	40 (25)	40 (30)	40 (30)	40 (NA)
	Width	mm	±5	1270	1120	1010	940	840	740	700
Standard
	Length	mm	±5	2730	2350	2160	2040	1880	1600	1500
Size
	Thickness	mm	±0.5	5~80	5~70	3~65	3~60	3~50	3~40	3~40

has good specific stiffness, specific strength. Compression, tensile, shear and bending strengths are excellent. PET foam core also has good dimensional stability and easy to process, suitable for a variety of processes. It is an ideal core material for lightweight & high-strength composite sandwich structures.It provides excellent fatigue resistance, impact resistance and very low water absorption. Heat and sound insulation are also very good.


Features:
High exothermic peak tempertaure resistance, up to 180C
High performance weight ratio, good impact resistance
Resistance to many chemicals, almost no water absorption
Low flammability, self-extinguishing from fire
Suitable for a variety of composite molding methods: Vacuum infusion, spray up, hand lay-up, vacuum bagging
Good impact strength
Low resin absorption
Good sound & thermal insulation

Specification:

Item	Standard	Unit		P80	P100	P120	P150	P200	P250
Density	ISO 845	Kg/m3	Average	80	100	120	150	200	250
			Tolerance	-6,+9	±10	±10	±15	±20	±30
Compression	ASTM D1621	MPa	Average	0.85	1.2	1.8	2.4	3.9	5.2
Strength			Minimum	-0.8	-1.1	-1.55	-2.2	-3.4	-4.8
Compression Modulus	ASTM D 1621	MPa	Average	73	100	115	140	200	235
			Minimum	-65	-90	-105	-125	-170	-210
Tensile Strength	ASTM D 1623	MPa	Average	1.4	1.8	2.2	2.5	3.2	4
			Minimum	-1.3	-1.6	-1.9	-2.2	-2.6	-3.6
Tensile	ASTM D 1623	MPa	Average	90	110	120	160	210	275
Modulus			Minimum	-80	-100	-105	-130	-180	-250
Shear	ASTM C 273	MPa	Average	0.55	0.8	0.9	1.25	1.7	2.05
Strength			Minimum	-0.45	-0.75	-0.8	-1.05	-1.5	-1.8
Shear	ASTM C 273	MPa	Average	13.5	23	27	35	51	70
Modulus			Minimum	-12.5	-21	-23	-30	-47	-65